What’s not to love about platinum? It’s the densest of the precious metals, can stand up to a lifetime of everyday wear, and is even hypoallergenic, making it a perfect pick for any bride. Take the time to become a platinum expert. As you master working with platinum, you can also teach the merits of why it may be the better choice for your customer’s lifestyle, earning trust, and ensuring a return to your store. Here are a few popular questions we often receive:

What is the melting temperature of platinum and other popular alloys?

Pure Platinum: 3140°F (1726°C)

Pt950/Ruthenium: 3266°F (1796°C)

Pt950/Cobalt: 3015°F (1657°C)

Pt900/Iridium: 3236°F (1780°C)

Which solder should I use?

Platinum melts at a high temperature, which may cause diamonds to frost over when exposed to such extreme heat. Because of this, we recommend that all stones be removed when welding or soldering with platinum solder on a platinum ring.


A few tips and tricks:

Try using Redi-Prongs® Platinum Round Retipping Kit to retip prongs around certain colored stones and diamonds. Simply flatten the surface of the prong that you want to retip using a small file. Then, heat the area and attach a prong cap (Redi-prong comes with pre-applied solder). Polish the prong and you are done.

What type of fuel do I use when working with Platinum?

Propane or natural gas is the best option for working with Platinum. These have less carbon content when compared to acetylene and will not contaminate your platinum.


Should I use flux?

Avoid the use of flux when joining platinum alloys. However, flux may be used when joining platinum alloys to gold alloys.

Which sandpaper grit is best for removing dents and scratches from a platinum ring?

360-400-500 abrasive paper


What people don’t always know is—

Platinum cobalt is slightly magnetic because of its similar structure to nickel. This alloy is ferromagnetic, so it should be kept away from magnetic bench shavings. Also, a magnet can be used to determine if a jewelry item is made from platinum cobalt.

Polishing tip

When polishing jewelry that has both platinum and gold elements, be sure the platinum is polished completely before polishing the gold. Gold polishes faster than platinum, so it is easy to over-polish the gold portion and ruin the piece.


Did you know: We use three different types of platinum here at Stuller—

  • For heads, we use platinum iridium because it is the brightest, whitest alloy available, thus making it ideal for setting gemstones and diamonds.
  • For die-struck pieces, we use platinum ruthenium as the fabricated metal.
  • For cast pieces, we use platinum cobalt because it is the desired alloy for casting.
  • For coined pieces, we use platinum cobalt in a combined process of casting and die striking.

In fact, using platinum cobalt for cast pieces means you get the benefit of a denser, more solid casting without the problems that porosity can create. The surfaces are smoother than platinum iridium and ruthenium immediately after casting, too.

Laser Welders are the best for working with platinum, saving time for your shop and increasing productivity, capabilities, and profits. This investment will pay for itself in no time.

When Joining Two Platinum Metals:

  • Platinum iridium to platinum iridium – weld
  • Platinum ruthenium to platinum ruthenium – weld
  • Platinum ruthenium to platinum iridium  – weld.
  • Platinum cobalt has a lower melt point than platinum ruthenium or platinum iridium, it cannot be welded to either PtRu or PtIr.
  • Platinum cobalt to platinum cobalt – use 1700C seamless.
  • To eliminate the dip in a solder seam, use a 1700C seamless solder.
  • If gold is melted into a platinum surface, remove the gold with a ball bur and fill it with platinum wire.

Tip: When in doubt, always solder.



Find more tips on working with platinum here.

Anything we missed? If you have a question, let us know in the comments below. We’ll work to help you get the answers you need.